Single pack water-based elastomeric coating with superior adhesion and corrosion protection. Excellent anti-corrosion properties, chromate and zinc free which can be applied by spray, brush and roller.

• Available in 20kg units

--

You'll know the original product - meet the improved addition to the Noxyde coatings family - single pack water-based elastomeric coating based on a silane modified acrylic binder with superior adhesion and corrosion protection. The product contains anti-corrosion pigments and is lead, chromate and zinc free which can be applied by spray, brush and roller.

Advantages:

• Superior adhesion

• High dirt pick up resistance

• 200% elastic coat does not crack or peel

• Excellent coverage of nuts, bolts and welds

• Dry fall: saves preparation & clean up time

Recommended Uses:

On iron, steel, special alloys, galvanised and metallised iron and steel, aluminium, copper, zinc, lead, etc. as rust prevention or waterproofing. For outside and inside use.

Diluted with 25% water as an adhesion primer coat on slightly or non porous substrates such as glass, smooth bricks and concrete, ceramics, tiles, etc.

Technical Data

Density (g/cm³): 1,25
Gloss Level: Satin
Gloss level at 60º: 24%
Solids Content in weight: 66%
Solids content in volume: 46%
Salt Spray Resistance: 1.248h salt spray resistance ISO 9227:2017

Drying Times
Touch dry: 1hr and 20 minutes
Dry to handle: 2 hours and 45 minutes
Dry to recoat: 24 hours
Fully cured: 2 weeks

Recommended Wet Film Thickness
380 µm

Recommended Dry Film Thickness
175 μm

Theoretical Consumption
Brush/Roller – 240 – 360 g/m²/coat
Airless – 360 – 600 g/m²/coat

Total consumption for optimal rust preventive protection 950 g/m² (in minimum 2 coats) = 350 µm dry film thickness